Abstract

In the current work, the fracture properties of epoxy polymers containing polysiloxane core shell rubber (CSR) nano-particles were studied. The effect of different cure rates and curing temperatures on the epoxy resin was also investigated. Single edge notched bend tests were performed to evaluate the fracture energy of the polymers. The fracture energy of the unmodified epoxy polymer increased significantly from 339 J/m2 to 3, 922 J/m2 due to the addition of 9 wt% of CSR nano-particles. Similarly, the fracture toughness for the unmodified polymer increased from 1.27 MPa m^1/2 to 3.42 MPa m^1/2 for an epoxy polymer containing 9 wt% of CSR nano-particles. Faster rates of curing, which can be achieved at higher cure temperatures are found to be detrimental to the toughness of the modified epoxy polymers

خلاصه

در این مقاله، خواص شکست اپوکسی پلیمرهای حاوی نانوذرات  لاستیکی هسته پوسته پلی سیلوکسان (CSR) بررسی شده است. همچنین اثر سرعت و دمای پخت روی رزین اپوکسی مورد مطالعه قرار گرفت. از تست خمشی تک ناچ جهت بررسی انرژی شکست پلیمرها استفاده گردید. به علت افزایش 9wt% نانوذرات CSR، انرژی شکست اپوکسی پلیمرهای اصلاح نشده به صورت قابل ملاحظه ای از 339J/m² به 3922j/m² افزایش یافت. همچنین، چغرمگی شکست پلیمر اصلاح نشده از 1.27MPa m^1/2 به 3.42MPa m^1/2 برای اپوکسی پلیمر حاوی 9wt% نانو ذرات CSR افزایش یافت. سرعت پخت سریعتر که در دمای پخت بالاتر حاصل می شود منجر به کاهش چغرمگی اپوکسی پلیمر اصلاح شده می شود.